Proflex® F1500 Clear Epoxy Primer

Proflex® 1500 Clear Primer is a unique, extremely flexible, two-component epoxy membrane. It is solvent-free and exhibits excellent tensile strength and elongation under ambient as well as colder temperatures.

ADVANTAGES

 

  • 100% solids for low odor during installation

  • Less hazardous.

  • Self-priming and leveling on properly prepared surfaces.

  • Self-leveling when sufficient material is applied.

  • Fills depressions, spalled areas and cracks.

  • Absorbs movement to help prevent reflective cracking.

  • Remains flexible over a wide range of temperatures.

 

SURFACE PREPARATION Surface and air temperature must be a minimum of 50° F. during installation and initial cure. Surface should be checked for soundness. Standard surface preparation practice should be followed, including thorough cleaning and drying.

 

Proflex® Primer comes as a two-part system, Part A catalyst and Part B epoxy liquid. Two parts of Part A are mixed with one part of Part B prior to application. Pot life is approximately 1 hour at which time the mixture begins to gel.

 

 

Examples of substrates that need to be coated with Proflex Primer® prior to application of EPDM Liquid Rubber® or Liquid ProPoly® F9601 are:

 

  • Wood

  • Plywood

  • Concrete

  • Rigid Foams

  • Previously Painted Surfaces

  • Spray On Urethane Foams

  • Smooth Aluminum, New Galvanized Steel, Glass and Plastics such as ABS, Polypropylene, PVC, Polystyrene, Acrylic, Hypalon and other Thermoplastic Olefin membranes must be primed with Proflex Primer®

 

To Order Proflex® F1500 Click Here.

 

IMPORTANT NOTE: It is important to know that you should not use water or water based products to clean your concrete. This will effect adhesion.

TYPICAL PROPERTIES (When mixed)

Mix Ratio:                                                                               2:1 by volume

Density:                                                                                  9.44

Viscosity (Brookfield):                                                            750 cps

Gel Time:                                                                               55 min.

Cure Time:                                                                             24 hours

Shore D Hardness (72 hrs):                                                   52

Adhesion (aged):                                                                   100% @ 730 psi

Impact Resistance:                                                                > 174 inch-lbs.

Mandrel Bend:                                                                       1/8” no crack

Color:                                                                                     Clear

 

                                                                                  7 days15 days

Tensile Strength – Ambient:                                      808 psi                                                    1390 psi

Tensile Strength – Chilled:                                        3900 psi                                                   6610 psi

Elongation – Ambient:                                               139 %                                                      132 %

Elongation – Chilled:                                                 68 %                                                         27 %

Modulus of Elasticity – Ambient:                               79.7 psi                                                     331 psi

Modulus of Elasticity – Chilled:                                 1150 psi                                                    1180 psi

Hot Tire Print                                                            No permanent imprint @ 2 hrs.,140°F

 

 

The information presented herein is furnished free of charge and is based on technical data that Advanced Rubber Coatings believes to be reliable. It is intended for use by persons having technical skill and is at their own discretion and risk. Since conditions of use are outside our control we make no warranties, express or implied, and assume no liability in connection with any use of this information. Nothing herein is to be taken as a license to operate or a recommendation to infringe any patents.