ProPoly F9601 Urethane | advancedrubbercoatings

Liquid ProPoly® Series 9600

The Liquid ProPoly® is a product of high solids 2 part Aliphatic Urethane. It differs only in anti-skid additives.

Liquid ProPoly® coating was formulated to incorporate the latest advancements in polymer technology. The objective was to develop a coating with superior durability that could be used on roofs, walls or foot traffic decks, had a 1 to 2 hour pot life plus fast cure.

Liquid ProPoly® has met these objectives.

Liquid ProPoly® Urethanes produce a tough yet elastomeric coating that is equally suitable for application on roofs, walls and siding, storage tanks as well as foot traffic surfaces. Non skid properties are obtained by incorporating the Anti-Skid Additive prior to application.

The Liquid ProPoly® Coatings produce a very smooth glossy surface with low dirt retention properties. This is desirable for Recreational Vehicles, Metal Roofs and Steel Tanks.Primer® F1500 Clear can be used over porous surfaces when a gloss finish is desired and Liquid ProPoly® topcoat can be applied within 3 days.

Traffic Decks should have non-skid surfaces. This is easily accomplished by incorporating the Anti-Skid Additive to Liquid ProPoly® prior to application.

Liquid ProPoly® coatings can be applied to both rigid as well as flexible substrates. It will have excellent adhesion when used with Proflex® F1500 Clear Primer.

Surface Preparation:

1. Substrate to be coated must be dry and free of dirt, debris and loose or peeling paint, asphalt based coatings must be removed.

2. Make any necessary repairs to ensure a structurally sound substrate prior to coating.

3. Corrosion on steel must be primed prior to application of Liquid ProPoly®

Mixing:

NOTE:Part B (catalyst) is extremely sensitive to moisture and water. Do not open can before ready to mix. If solidified, then it needs to be replaced.

Part A is pigmented and should be uniform without lumps or hard settling. Examine Part B to determine that it is clear and has not solidified. This part can solidify by reacting with moisture from the atmosphere, keep containers tightly closed when not in use. Mix equal volumes of Parts A and B using a drill mixer. Scrape sides of container and mix with rest of material.

Coverage:

Theoretical coverage = 1426 ft. at 1 mil film thickness.

ProPoly® F9601 Urethane

Total Thickness

ft²/gal: film thickness wih primer

200 6 mil 16 mil

100 14 mil 24 mil

75 19 mil 29 mil

50 28 mil 38 mil

(Proflex Clear Primer® = 10 mil thickness)

Availability:

Propoly urethane with catalyst is available in 2,4,6,10 gallon sizes. Color: White.

To Order ProPoly® F9601 Click Here.

Pot Life:

A chemical reaction begins after parts A & B are mixed and this produces some heat. When the heat builds up in the container it accelerates the reaction and causes a rapid increase in viscosity. The time interval to reach a difficult to apply viscosity is the pot life.

At 60º F Pot Life is 2.7 hrs.

At 72º F Pot Life is 1.5 hrs.

At 85º F Pot Life is 1.0 hrs.

Cure:

Film cure rate is shortened with increasing temperature. At 72º F the set to touch time for the clear and White coating is 2.5 to 3 hours and 3.0 to 3.5 hours for the colors. The coating can be handled after 6 hours and take light foot traffic after 24 hours. Vehicular traffic can begin after 48 hours.

Thinning:

Do not thin product if application is by squeegee and roller. Use MEK (Methyl Ethyl Ketone) if needed for spray application and clean-up.

Recoating:

Although the Liquid ProPoly® film reaches sufficient cure to handle or even walk on in less than 12 hours it requires approximately 7 days to reach full cure. Touch up or a second coat of Liquid ProPoly® may be applied within that period. If Liquid ProPoly® is more than 7 days old the surface of the film will have reached a cure condition that would prevent a second coat from adhering to it. In that event either abrade (sand) the first coat or apply Proflex Primer® prior to recoating with Liquid ProPoly®

Useful Information:

You will have more time to distribute the material when the mixed product is emptied from the container onto substrate(surface) within 45 minutes.
Addition of 10-15% solvent extends pot life.
When spraying always put pump suction tube into newly mixed pail and then add remainder of previous pail.
Flush spray pump and hoses with MEK (Methyl Ethyl Ketone) solvent every two hours to prevent product from curing in the hose when spray application takes more than two hours to complete.
Do not apply Liquid ProPoly® if rain is forecast within 12 hours.

Product Data

Chemical Type Two Component Aliphatic Urethane

Solid Content 88.9% by Volume

Weight per Gallon 10.64 lbs.

Mix Ratio 1:1 by volume

Spread Rate at 1 mil 1421 sq. ft.

Viscosity Initial 3000 cp mixed

Viscosity After 45 min. 9000 cp mixed

Pot Life 1.5 hr at 72ºF; 1 hr at 85ºF

Tensil Strength 2900 psi

Elongation 150%

Flash Point over 130ºF

Compatible Solvents MEK (Methyl Ethyl Ketone)

VOC 93g/l (0.775 lbs/gal)

Storage Stability 6 mo. to 1 yr.

The information presented herein is furnished free of charge and is based on technical data that Advanced Rubber Coatings believes to be reliable. It is intended for use by persons having technical skill and is at their own discretion and risk. Since conditions of use are outside our control we make no warranties, express or implied, and assume no liability in connection with any use of this information. Nothing herein is to be taken as a license to operate or a recommendation to infringe any patents.

Advanced Rubber Coatings